ASTM A519 4140 tubing

ASTM A519 4140 tubing

A519-4140 material is stocked in the annealed, normalized or quenched and tempered conditions. The heat treated material is controlled to L80, P110, Q125 or the customer’s specified properties. The material is weldable but requires a pre-heat before welding.

4140-tubing

A519-4140 material is stocked in the annealed, normalized or quenched and tempered conditions.

Seamless Tubing sizes used in the oil and gas industry for above ground and down hole applications.
Yaang Steel can supply  4140 Tubing:
  • A519-4140
  • L80, P110, Q125 heat treated mechanicals
  • 2.5 to 15inch OD
  • 0.375inch to 4.0inch
Key: AISI 4140 tubing, ASTM A519 4140 tubing, 4140 alloy tubing

TOLERANCES

Condition OD Wall
Annealed or Normalized ASTM A519 ASTM A519
Quenched and Tempered +/-1% +/-12.5%

Mechanical Properties
The minimum wall thickness at any point shall not be more than 12.5% under the nominal wall thickness specified.

Mechanicals Heat Condition Hardness Yield Tensile
A519-4130 / 4140 Quenched and Tempered 28-32 RC Not Tested Not Tested
API 5CT L80 in 4519-4100 Quenched and Tempered 18-22 RC 80 – 95 ksi 95 ksi min
API 5CT P110 in 4519-4100 Quenched and Tempered 30-36 RC 110 – 140 ksi 125 ksi min
API 5CT Q125 in 4519-4100 Quenched and Tempered 32-36 RC 125 – 150 ksi 135 ksi min

Mechanical Tubing Delivery Condition : 

  • As different requirements,It including Size, Packing,Fixed Length,Random Length,And Different Annealing condition etc. (BK,NBK.Bright annealing …)
  • CW-Cold Worked SR-Stress Relieved A-Annealed N-Normalized

ASTM A519 Standard Specification for Seamless Carbon and Alloy Steel Mechanical Tubing

About NCTV

www.yaang.com provide a wide range of steel products as Steel pipe, Steel pipes and seamless pipes, Alloy pipes, Pipe fittings, Composite steel pipe used in the industry, construction etc.

Leave a Reply

Your email address will not be published. Required fields are marked *

*

Scroll To Top